Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.
Scientific Reports volume 13, Article number: 6306 (2023 ) Cite this article Sulphur Brown Gd
In this work, sulphur doped copper ferrites (S-CuFe2O4) photocatalysts were successfully synthesized for the first time using the facile hydrothermal method. The as-synthesized photocatalysts were characterized through XRD, Raman, TGA, FT-IR, UV–Vis-DRS, SEM, EDX and PL techniques. The results revealed that doping with sulphur has been found to be a suitable alternative that causes strain in the lattices as anions replace the oxygen from the CuFe2O4 nanostructures. Due to sulphur dopants, photocatalysts are able to efficiently trap and transfer the photoinduced charges, which readily suppress charge recombination. A UV–Vis spectrophotometer was used to monitor the degradation of selective toxic organic dyes (RhB, CR, MO, and CV) in aqueous media. The dye degradation results provide evidence for the surprisingly superior performance of S-CuFe2O4 over pristine CuFe2O4. On the basis of its efficiencies, this work can be assigned as an excellent candidate for photocatalysis science.
Water pollution is one of the world's most serious environmental problems. Industrialization produces wastewater that contains a variety of harmful pollutants1. The most prevalent pollutants are synthetic organic dyes, which are widely used in variety of industries, and pose severe threats to the aquatic environment2. Azo dyes that are widely used in textile industries are proven to be carcinogenic and killers for liver cells3. Similarly, methyl orange (MO) and crystal violet (CV) are toxic, water-soluble anionic azo dyes with complex chemical structures that cause gastrointestinal, respiratory, and skin irritations. Congo red (CR) is an azo dye that is carcinogenic, mutagenic, and causes reproductive problems4. Rhodamine B (RhB) is a fluorescein dye that causes skin and eye irritation and is toxic if swallowed. These fluorescein dyes are extremely cytotoxic to mammalian tissues and cause morphological and genetic changes5,6. Thus, polluted water is becoming a challenge, especially for the urban communities lying near industrial zones. Therefore, it is crucial to remove these dyes from wastewater using an economical approach7,8.
Various strategies have been developed for the degradation of dyes in contaminated water. Adsorption, electrochemical deposition, redox reactions and biological treatment are examples of these methods9,10. However, due to the inherent toxicity, production of secondary pollutants and high cost of these approaches, these methods proved ineffective11. More research is obligatory to develop cost-effective, stable and risk-free materials to address these issues. Photocatalytic dye degradation is a low-cost, versatile and energy-efficient process that breaks down organic dyes in water using light and a catalyst12,13. For this purpose, various metal oxides, sulphides, quantum dots, noble metal nanoparticles, polymers, metal and non-metal doped hybrid materials, graphene-based materials, gold nanoclusters and transition metal ferrites have been used14,15,16,17,18,19,20,21,22,23,24. Among these, nanomaterials of transition metal ferrites have low cost, high chemical stability, a large surface area, reusability and catalytic properties25.
For dye degradation applications, a number of ferrites including spinel ferrites, have been reported to be used as catalysts26. Thus, spinel ferrites are the type M2+M23+O4 class of compounds that have attracted great attention for dye degradation studies27,28. The typical formula for spinel ferrites is MFe2O4, where M = Zn, Mn, Ni, Cu, etc. The composition and structure of ferrites influence their ability to adsorb substances, which is dependent on their morphology and inherent crystal structure29. CuFe2O4 is a spinel-type material with a narrow band gap, photochemical stability and visible light activity28. Moreover, its low toxicity, cost-effectiveness, versatility, and recyclability make it an attractive catalyst for water purification applications30,31. Various methods have been reported to synthesize spinel ferrites microstructures such as sol–gel, photo as well as electro deposition, solid state reaction, hydrothermal method and coprecipitation32. Hydrothermal method is preferred due to versatility, uniformity, purity and ease of synthesis33.
However, due to the rapid recombination of photo-generated charge carriers, it is necessary to improve the effectiveness of CuFe2O434. To improve photocatalytic efficiencies, a variety of techniques, such as construction of nanocomposite35, p-n junctions36 and metals and non-metals doping37 have been used. Selective doping can recast the band structure by generating quasi-stable energies38. Recently, sulphur dopants on g-C3N4, graphene sheets39,40 and ZnO have been reported to improve photocatalytic applications41. Moreover, because of the significant difference in size and electronegativity between S and O, S dopants modifies the optical, electrical and photocatalytic properties of semiconductor oxide42.
To modify the conventional ferrites and acquire the advantage of S-dopants, the hydrothermal method was adopted to synthesize S-doped copper ferrite (S-CuFe2O4) photocatalysts. The as-prepared CuFe2O4 and S-CuFe2O4 catalysts were used for degradation of the selective dyes like rhodamine B (RhB), congo red (CR), crystal violet (CV) and methyl orange (MO) as a probe reaction. The results demonstrate that S-CuFe2O4 photocatalysts demonstrate higher photocatalytic efficiencies as compared to pristine CuFe2O4.
Copper ferrites were synthesized by hydrothermal method as follows: Solutions of 0.1 M copper nitrate and 0.2 M iron nitrate magnetic stirred for 30 min. After that, 0.01 M glucose solution was transfer to above solution and left it for stirring (22 h, 50 °C), the preparations of solutions were explained in (supporting information) section. The obtained mixture solution was then sonicated for 30 min by adjusting the sweep frequency (≈ 37 kHz, 300W). The final solution was kept in autoclave (Sanfa, DHG-9030) for 6 h at 140 °C, which is then cooled down and filtered by using high grade filter paper (WHA 1001325, Grade-1). The obtained precipitates were washed thoroughly using deionized water and then with absolute ethanol. To prepare sulphur doped copper ferrites (S-CuFe2O4), 500 mg of CuFe2O4 powder was transferred to autoclave reactor and appropriate amount of 1% thiourea solution (5 mg, 0.01 M) was added into this mixture and mixture was again kept in autoclave for 6 h at 140 °C. The synthesis scheme was illustrated in Fig. 1.
Scheme used for the synthesis of CuFe2O4 and S-CuFe2O4.
To predict the morphology and crystal structures of S-CuFe2O4, powder X-ray diffraction (XRD) results were obtained at Philips-X Pertpro, with Cu kα radiation, λ = 1.5406 Å. For the surface morphology of as-prepared catalysts, SEM analyses were conducted on a Field Emission Scanning Electron microscope (FEI-Nova Nano SEM-450). Energy dispersive X-ray analysis (EDX, Horiba 7593 H) afforded the chemical composition of the prepared catalysts. The ultraviolet–visible-diffuse reflectance (UV–Vis-DRS) results were obtained at AvaSpec-2048 TEC spectrometer. The Photoluminescence (PL) results were recorded using Fluorescence spectrometer (LS-45, Perkin Elmer), where PL intensities were measured at 300–650 nm range. Dye degradation experiments were performed using UV–Vis spectrophotometer (PerkinElmer/λ-365. TGA was performed using TG209 F3Tarsus®, NETZSCH Germany. Fourier Transform Infra-Red (FT-IR) analyses were performed on Bruker Tensor-27. Raman analysis was done by using JASCO NRS-5000/7000 dispersive Raman spectrometers.
The photocatalytic degradation properties of pristine CuFe2O4 and S-CuFe2O4 were investigated in the presence of visible-light radiations within Pyrex reactor. The photoreactor was cylindrical, having a 500 mL volume capacity with an 8 cm internal and 10 cm external diameter. In order to prevent light emission into the surrounding environment, the outer wall of the reactor was covered by aluminum foil. The cool water was allowed to circulate around the walls of the reactor in order to keep it at room temperature. A halogen lamp having λ ˃ 400 nm was used as a radiation source. The 10 mg amount of photocatalyst was fixed for each photoreaction at pH 7 for 15 ppm dye solution (vol = 100 mL). Prior to photoreaction, the solutions were stored in the dark (absence of light) to ensure the adsorption equilibrium. For the photoreaction, a halogen lamp was fixed at a distance of 30 cm from the reactor. The photocatalytic degradation efficiency was examined at different time intervals using a spectrophotometer (PerkinElmer/λ-365).
The synthesis procedure of our S-CuFe2O4 photocatalysts is shown in Fig. 1 (see details in the “Experimental” section). To remove the impurities and enhance the crystallinity, the as-synthesized photocatalysts were calcined at 350 °C for 3 h.
The phase purity and crystalline nature of as-prepared product was determined by XRD. The XRD pattern of copper ferrite nanostructures is shown in Fig. 2a. The XRD patterns exactly match the standard JCPDS file No. 77-001043. The diffraction peaks of as-synthesized catalysts are located at 18.34°, 30.17°, 35.54°, 37.18°, 43.19°, 53.59°, 57.13° and 62.744° that are associated with Millar indices as (111), (220), (311), (222), (400), (422), (511) and (440) respectively. These XRD patterns indicate that as-synthesized catalysts emphasize cubic spinel structures, where Fe+3 ions occupy octahedral while Cu+2 ions occupy tetrahedral sites. It has been noted that due to sulphur doping major peaks shifts to the lower 2 theta whereas intensity of diffraction peaks has been observed to be decreased as well. The XRD results depict that the replacement of larger sulphur anions was accomplished with the smaller oxygen ions in the CuFe2O4 structure. No other crystalline phases of Fe2O3, FeS or CuS were detected that confirm the purity of the catalysts, some extra peaks beyond 65° were observed due to some CuO contents44. The sharpness of peaks indicates that the designed catalysts of this work are highly crystalline in nature. The crystalline sizes of pure CuFe2O4 and S-CuFe2O4 have been calculated by using Debye‒Scherrer’s Formula in Eq. (1).
where λ is 1.54060 Å, β is FWHM and θ is diffraction angle (Cu‒Kα). The Williamson‒Hall method was also used to calculate the crystallite size of both pure CuFe2O4 and S-CuFe2O4 Eq. (2).
where d is crystalline size, K is constant = 0.94, ε is constant = 145. The crystallite size (D) was calculated using the Scherer formula and Williamson‒Hall method are tabulated in Table 1, whereas, the Williamson-Hall plots are depicted in Fig. S1.
(a) XRD patterns exhibited with zoomed image in the inset, (b) Raman spectrum, (c) FT-IR spectrum of CuFe2O4 and S-CuFe2O4, (d) TGA of S-CuFe2O4 photocatalyts.
Raman spectroscopy is an efficient technique for direct probe of structural transformation, cation redistribution, bonding in metal oxides and lattice distortion30. Figure 2b represents Raman spectra of CuFe2O4 and S-CuFe2O4. Group theory analysis yields four Raman active modes denoted by A1g, Eg and two T2g modes in range of 200–800 cm−131. The A1g mode observed at ∼ 703 cm−1, Eg mode at ∼ 273 cm−1, the two T2g modes ∼ 482 cm−1 and ∼ 552 cm−1. The obtained Raman frequency relies on the Fe(Cu)–O bond length, that varies with the major factors, like phase transformation, lattice distortion and cationic redistribution32. It has been noted that sulphur dopants in copper ferrite shift the Eg mode slightly to a smaller wave number (273 to 270 cm−1). Lattice distortion was observed, between two T2g modes ascribed majorly due to the sulphur dopants as compared to oxygen contents present in catalysts33.
The Fourier transforms infrared spectrum of CuFe2O4 and S-CuFe2O4 nanoparticles are shown in Fig. 2c. In the present work, major FTIR peak observed at 530 cm−1 is due to M–O vibration of tetrahedron where M represents copper or iron. Similarly, peak observed at 436 cm−1 was referred to the stretching of octahedron planes of spinel copper oxides. The broad band located at around 3500 cm−1 are related to bending vibration of O–H, which correspond to the hydroxyl groups or absorbed water molecules over the catalyst’s surfaces. It is obvious that upon doping sulphur content, the metal sulphur vibrations lies at 500 cm−1, exhibit low intensity than that of the Cu–O/Fe–O vibration peaks. FTIR patterns located approximately at 1020–1030 cm−1 is due to the C–N stretching, which are likely to be caused by thiourea46. These stretching vibrations are also observed by other researchers working on S dopants47. These nitrogen/carbon (N–C) vibrations are absent in the FT-IR spectra of pristine CuFe2O4.
Thermo gravimetric analysis of as-synthesized S-CuFe2O4 (without calcination) was performed to investigate physical behavioral changes (Fig. 2d). These evaluations were performed under N2 atmosphere; within the temperature range 35–800 °C where increment in heating rate was maintained 5 °C/min. It has been observed that 1.6% weight loss was observed up to 165 °C, this loss can be attributed to the volatilization of absorbed water and solvent molecules48. Moreover, further 2.4% weight loss up to 220 °C was observed, endorsed to decomposition of metal hydroxide48,49. Afterwards, by increasing the temperature up to 800 °C no weight loss was observed, this exhibited excellent thermal stability of S-CuFe2O4 nanoparticles.
The morphologies of pristine CuFe2O4 and S-CuFe2O4 nanostructures were investigated by SEM (equipped with ETD/TLD detector). The SEM images of pristine CuFe2O4 are demonstrated in Fig. 3a,b. The results show that the particles are agglomerated and have irregular flacks-like morphologies. The particles have a tendency to agglomerate in clusters due to the attractive forces (i.e., magnetic dipole–dipole)50. Whereas, the SEM results of as-prepared S-CuFe2O4 catalysts are shown in Fig. 4a–d at different magnifications (i.e., 5 µm, 2 µm, 1 µm and 500 nm). It is clear from SEM results that by doping with sulphur, the flakes-like morphology of catalysts became more regular and agglomeration was reduced, which indicate the porosity of catalysts51. Thus, more active sites are available for photocatalytic reactions. These results depict that S-doping enhances the surface area and assist to increase the catalytic activity of CuFe2O4. EDX analyses provide valuable information on the composition and distribution of elements. The EDX results of as-synthesized pristine CuFe2O4 and S-CuFe2O4 photocatalysts are illustrated in Figs. 3c and 4e, respectively. The EDX results reveal the relative amounts of copper, iron, oxygen and sulphur in the material that are tabulated in Table S1 and S2 for pristine CuFe2O4 and S-CuFe2O4 photocatalysts respectively. Results have confirmed the purity and existence of sulphur dopants in CuFe2O4 photocatalysts.
SEM images of pristine CuFe2O4 at (a) 2 μm, (b) 500 nm, (c) represents the EDX analysis.
SEM images of S-CuFe2O4 at (a) 5 μm, (b) 2 μm, (c) 1 μm and (d) 500 nm, whereas (e) represents the EDX analysis.
The optical properties of pristine CuFe2O4 and S-CuFe2O4 were investigated by their UV–Vis-DRS study. The UV–Vis-DRS has advantage over UV–Vis absorption spectroscopy specifically to obtain the optical properties of powdered sample because it has less scattering effects than the absorption of liquids52. Figure 5a illustrates an absorption edge that indicates the Urbach resemblance absorption tail within visible region53,54. CuFe2O4 shows maximum absorption at ~ 688 nm, corresponding to its optical band gap i.e. Eg = 1.80 eV. Sulphur doping slightly red-shifted the visible absorption to around ~ 696 nm (Eg = 1.78 eV), showing excellent visible light response which results in higher photocatalytic activities, the band gap energy plot showed in Fig. 5b. The optimal band gap of pure and doped CuFe2O4 was determined by Eq. (3).
(a) UV–Vis-DRS (b) Band gap measurements for allowed transitions (c) PL results of CuFe2O4 and S-CuFe2O4where (d) represents the λmax of CR, CV, MO and RhB dyes.
The photoluminescence (PL) of as-synthesized photocatalysts provides the fundamental information to determine the photo-induced electron–hole (e‒/h+) pairs to trap and transfer processes. Figure 5c represents the comparative results for CuFe2O4 and S-CuFe2O4 which exhibit the broad peaks at 421 nm, 468 nm and 553 nm55. The decrease in the intensity in case of S-CuFe2O4 indicates the sulphur incorporation56. Moreover, this decrease intensity evidenced a greater transfer of electrons to active centers. PL peak at 468 nm corresponding to blue emission is due to imperative defects associated with the interface traps existing at the grain boundaries. Similarly, the peak at 553 nm corresponds to defect sites of oxygen vacancies. In S-CuFe2O4 emission is slightly shifted to 549 nm, attributed to the appearance of electronic levels of intrinsic characteristics57. It specifies that back recombination of electrons and holes are remarkably lower in case of S-CuFe2O4 catalysts. Due to doping of sulphur, several mid-gap states are formed between valance bands as well as in conduction bands within the structures of prepared catalysts. These mid-gap energy states result in electron/hole pair separation successively because sulphur serves as a charge-separating center58. In PL spectroscopy, a broader peak reveals better electron–hole separation, while high intensity peaks exhibit fast electron–hole recombination59. It is obvious from the PL spectra that S-CuFe2O4 display highly enhanced photocatalytic performance due to an efficient charge carrier separation60.
Figure 5d shows lambda max (λ-max) values for selective four toxic dyes such as CV, RhB, CR and MO having wavelength maxima at 590, 550, 500 and 460 nm respectively. The basic information and structure of selected dyes are demonstrateds in supporting information. The degradation results of aforementioned dyes over as-prepared photocatalysts were monitored at different time intervals in 300‒800 nm range. The results for the removal of RhB shown in Fig. 6a, indicate that S-CuFe2O4 photocatalysts adsorb 20.2% (302 mg/g) dye in the absence of visible light (dark). This adsorptive removal is accomplished without change in their λ-max. The amount of adsorbed dye at equilibrium qe (mg/g) was calculated by using Eq. (4):
where m is catalyst weight, V (L) is volume of solution and Co and Ce are concentrations at initial and equilibrium state of RhB solution61. Then sample was irradiated with visible light to examine the photocatalytic efficiency of the S-CuFe2O4. After 100 min, the concentration of degraded dye reached to ~ 99%. Comparison of degradation efficiency of pristine CuFe2O4 with S-CuFe2O4 shows 34% difference, see Fig. 7a. On the basis of PL and UV–VIS spectrophotometric studies, it could be concluded that presence of sulphur has enhanced the photocatalytic efficiency of copper ferrites by decreasing the electron hole recombination47. Rhodamine B has one carboxylic acid (‒COOH) and two amino groups (‒NH2). Ethyl molecules are electron promoters and donate electron to xanthene rings, as a result shifting the λmax to higher wavelength62. The higher λmax is due to electron donating effect of ethylene molecules. During the photoreaction, ethylene molecules are removed (de-ethylation), due to which the absorbance shifts towards lower wavelength called blue shift. It is observed that λmax in the graph shifted from 550 to 498 nm. It has been obvious that, blue shift may arise due to energy difference between HOMO and LUMO when rhodamine B is grafted with S-CuFe2O4 catalysts. HOMO being filled; its electrons get attracted to the polar S-CuFe2O4 by weak dipole–dipole interactions. This attraction lowers the energy of HOMO while empty LUMO energy states of catalysts remain unaffected. This transition shifts the λmax to the lower wavelength63. Besides this, the appearance of blue shift is due to the step by step N-de-ethylation64. This de-ethylation gives rise to N,N,N-triethylrhodamine, N,N-diethyl rhodamine and N-ethyl rhodamine. The final photo-degraded product is assumed to be a completely de-ethylated compound (rhodamine) that has characteristic absorbance maximum at 498 nm65.
(a) RhB, (b) CR, (c) MO and (d) CV degradation results.
(a) Comparison of % degradation of RhB, CR, MO and CV using pristine (yellow) and S-doped CuFe2O4 (blue) photocatalysts and (b) recyclability tests of S-CuFe2O4 photocatalysts for MO degradation.
Figure 6b represents absorption spectra of Congo red (CR) at different time intervals. Photoreaction of CR dye solution by S-CuFe2O4 photocatalysts starts after it attains equilibrium between adsorption and desorption in the dark (no light). This adsorption of dye in dark is due to the attraction of two oxygen atoms of sulfonate groups (CR dye) with surfaces of catalysts65. This removal is accomplished by parallel decrease in intensity of both peaks without change in their λmax, that is 340 nm for naphthalene rings and 500 nm for π-π* azo bonds66. After that, it was irradiated with visible light in order to initiate photocatalytic degradation. The absorption spectrum of CR shows two distinct peaks; peak at 500 nm is due to π-π* azo bonds and second peak at 340 nm is due to naphthalene rings. Actually, π-π* azo bonds are degraded easily as compared to naphthalene ring. After 100 min, the dye is almost completely removed due to destruction of its chromophoric structure in the vicinity of azo-linkages67.
Figure 6c represents absorption spectra of methyl orange (MO). The UV–vis spectra of methyl orange have a distinct broad band in the visible region, with maximum absorption at 460 nm due to the chromophore structure of the dye68. It is clear from results that after 70 min, the dye has degraded as a result of photoreaction with S-CuFe2O4 photocatalysts. This is due to the destruction of homo- and hetero polyaromatic rings present in methyl orange69. It has been investigated that during photoreaction, the –N=N– double bond breaks and simple phenyl rings are formed with amine groups as degraded products70.
Crystal violet (CV) degradation is exhibited in Fig. 6d which represents a sharp peak at about 590 nm. Previously reported studies explain that the degradation of crystal violet dye can take place via different mechanisms such as N-demethylation, chromophore cleavage and breaking in ring structure71. The degradation mechanism and pathway depends on the type of catalysts, degradation method and oxidizing agents used72. After 50 min, the violet color of dye solution had completely faded away. The comparative efficiencies of reported ferrites as-well as-prepared S-CuFe2O4 are illustrated in the Table 2.
Figure 7a illustrates the degradation efficiencies of S-doped CuFe2O4 in comparison with pristine CuFe2O4 for RhB, CR, MO and CV. After 100 min, 99% RhB was degraded by S-doped CuFe2O4 but pristine CuFe2O4 was able to degrade only 65% of it. Similarly CR was degraded to 98% by S-doped CuFe2O4 and 64% by pristine CuFe2O4 when measured after 100 min. 97% of MO was degraded by S-doped CuFe2O4 and 63% degradation occured with pristine CuFe2O4 after 70 min. For CV, 98% of dye degradation occured in only 50 min by S-doped CuFe2O4 and 68% in presence of pristine CuFe2O4. It could be concluded that S-CuFe2O4 nanostructures are more efficient photocatalysts as compared to the pristine CuFe2O4 because sulphur atoms introduce new active sites that enhance the interactions with the adsorbed dye molecules. Moreover, sulphur dopants modify the electronic structure of the photocatalysts, leading to changes in the bandgap and energy levels. This improves the separation of electron–hole pairs and reduces recombination, leading to more efficient use of the generated charge carriers for dye degradation. Another advantage associated with the use of S-CuFe2O4 photocatalysts is its good magnetic properties that allows it to be easily separated from reaction mixture by using external magnet. This separation technique is much easier, faster and efficient as compared to other conventional techniques such as filtration and centrifugation86. This also eliminates the risk of secondary pollution from catalysts as well as its full utilization for long times. The recyclability tests were performed for each cycle after careful washing and drying. Figure 7b shows recyclability results of S-CuFe2O4 for MO degradation. After being used three times for the degradation of MO, a slight difference in catalyst’s efficiency was observed due to loss of catalyst during recovery process.
The degradation mechanism of MO, RhB, CV and CR dyes are shown in Fig. 8. In absence of light, dyes are adsorbed on the surface of photocatalysts. When visible light is irradiated, photoreaction is governed by the excitation of electrons and holes. The electrons start to migrate from valance band to conduction band of photocatalysts. The available electrons at the conduction bands levels readily react with oxygen to generate superoxide radicals (⋅ O2‒). These superoxide radicals (⋅ O2‒) react with dyes and convert them to degraded byproducts87. At the same time, holes available in valance band levels of catalysts oxidize the dyes over the surfaces of catalysts. Presence of sulphur in the catalysts not only captures electrons but also prevents the recombination of charges (back reaction) and also can produce superoxide radicals (⋅ O2‒) over active sites of catalyst by transporting electrons to oxygen47. Moreover, holes oxidize the H2O molecules into ˖OH radicals, these hydroxyl radicals further enhance the dye adsorption at the surfaces of catalysts88,89. Due to higher dye adsorption at catalysts surfaces, rate of dye degradation is readily increased (Scheme 1).
Photocatalytic dye degradation reaction over S-CuFe2O4 photocatalysts.
Photocatalytic reactions involved in dye degradation.
In this work, CuFe2O4 and S-CuFe2O4 photocatalysts were successfully synthesized by employing hydrothermal methods. For structural morphologies XRD, Raman and FT-IR techniques were subjected to confirm crystallinity and sulphur doping. The results depicts that the doping of non-metallic anionic sulphur causes strain in the lattice and enter the lattice as anions by replacing oxygen. SEM results confirm that sulphur doping reduces the agglomeration and increases the actives cites for photoreactions. EDX confirms the presence of sulphur whereas TGA confirms the stability of as-synthesised S-CuFe2O4 at higher temperatures. PL results gave evidences that sulphur was capable to act as electron trapping centre which suppressed the recombination of charges during the photoreaction. The CuFe2O4 and S-CuFe2O4 photocatalysts were used to degrade RhB, CR, MO and CV dyes, results revealed that doping of sulphur boosts the photocatalytic degradation reactions. It has been found that by using S-CuFe2O4, RhB degradation efficiency has been increased from 65 to 99% within 100 min. The dye degradation results of this work assure the superior performances of S-CuFe2O4 than pristine CuFe2O4. On the basis of photocatalytic efficiencies, this work can be assigned as excellent candidate for photocatalysis applications.
All data used and analyzed in current work are included in this article and SI file.
Ahmed, J., Thakur, A. & Goyal, A. Industrial Wastewater and Its Toxic Effects (2021).
Khairnar, S. D. & Shrivastava, V. S. Facile synthesis of nickel oxide nanoparticles for the degradation of methylene blue and Rhodamine B dye: A comparative study. J. Taibah Univ. Sci. 13(1), 1108–1118 (2019).
Article Google Scholar
Khairnar, S. D. et al. Adsorptive and photocatalytic removal of carcinogenic methylene blue dye by SnO2 nanorods: An equilibrium, kinetic and thermodynamics exploration. SN Appl. Sci. 2, 1–12 (2020).
Article Google Scholar
Raval, N. P., Shah, P. U. & Shah, N. K. Adsorptive amputation of hazardous azo dye Congo red from wastewater: A critical review. Environ. Sci. Pollut. Res. 23(15), 14810–14853 (2016).
Article CAS Google Scholar
Mittal, A. et al. Adsorptive removal of hazardous anionic dye “Congo red” from wastewater using waste materials and recovery by desorption. J. Colloid Interface Sci. 340(1), 16–26 (2009).
Article CAS PubMed ADS Google Scholar
Culp, S. et al. Mutagenicity and carcinogenicity in relation to DNA adduct formation in rats fed leucomalachite green. Mutat. Res./Fundam. Mol. Mech. Mutagen. 506, 55–63 (2002).
Article Google Scholar
Haque, E. et al. Adsorptive removal of methyl orange from aqueous solution with metal-organic frameworks, porous chromium-benzenedicarboxylates. J. Hazard. Mater. 181(1–3), 535–542 (2010).
Article CAS Google Scholar
Rai, A. et al. Sustainable treatment of dye wastewater by recycling microalgal and diatom biogenic materials: Biorefinery perspectives. Chemosphere, 305, 135371 (2022).
Article CAS PubMed ADS Google Scholar
Lv, X., Lam, F. L. Y. & Hu, X. A review on bismuth oxyhalide (BiOX, X= Cl, Br, I) based photocatalysts for wastewater remediation. Front. Catal. 2, 4 (2022).
Article Google Scholar
Srivastava, V. et al. Green synthesis of biogenic silver particles, process parameter optimization and application as photocatalyst in dye degradation. SN Appl. Sci. 1, 1–15 (2019).
Article Google Scholar
Singh, P. K. & Singh, R. L. Bio-removal of azo dyes: A review. Int. J. Appl. Sci. Biotechnol. 5(2), 108–126 (2017).
Article MathSciNet CAS Google Scholar
Bhatia, S. K. et al. Wastewater based microalgal biorefinery for bioenergy production: Progress and challenges. Sci. Total Environ. 751, 141599 (2021).
Article CAS PubMed ADS Google Scholar
Khairnar, S. D. & Shrivastava, V. S. Photocatalytic degradation of chlorpyrifos and methylene blue using α-Bi2O3 nanoparticles fabricated by sol–gel method. SN Appl. Sci. 1, 1–10 (2019).
Article CAS Google Scholar
Yadav, S. et al. A review on degradation of organic dyes by using metal oxide semiconductors. Environ. Sci. Pollut. Res. 29, 1–21 (2022).
Yang, Q. & Hao, J. Synthesis of metal sulfides via ionic liquid-mediated assembly strategy and their photocatalytic degradation of dyes in water. Colloids Surf. A 633, 127848 (2022).
Article CAS Google Scholar
Alshorifi, F. T., Alswat, A. A. & Salama, R. S. Gold-selenide quantum dots supported onto cesium ferrite nanocomposites for the efficient degradation of rhodamine B. Heliyon 8(6), e09652 (2022).
Article CAS PubMed PubMed Central Google Scholar
Lu, Q. et al. Photocatalytic degradation of methyl orange by noble metal Ag modified semiconductor Zn2SnO4. Mater. Sci. Semicond. Process. 138, 106290 (2022).
Article CAS ADS Google Scholar
Du, X.-H. et al. BODIPY-linked conjugated porous polymers for dye wastewater treatment. Microporous Mesoporous Mater. 332, 111711 (2022).
Article CAS Google Scholar
Dake, D. et al. Photocatalytic performance of graphene-based Cr-substituted β ZnS nanocomposites. Appl. Phys. A 128(4), 1–20 (2022).
Article Google Scholar
Chandra, S. et al. Highly luminescent gold nanocluster frameworks. Adv. Opt. Mater. 7(20), 1900620 (2019).
Article CAS Google Scholar
Ali, N. et al. Enhanced photodegradation of methylene blue with alkaline and transition-metal ferrite nanophotocatalysts under direct sun light irradiation. J. Chin. Chem. Soc. 66(4), 402–408 (2019).
Article CAS Google Scholar
Gnanamoorthy, G. et al. Photocatalytic properties of amine functionalized Bi2Sn2O7/rGO nanocomposites. J. Phys. Chem. Solids 118, 21–31 (2018).
Article CAS ADS Google Scholar
Gnanamoorthy, G. et al. Global popularization of CuNiO2 and their rGO nanocomposite loveabled to the photocatalytic properties of methylene blue. Environ. Res. 204, 112338 (2022).
Article CAS PubMed Google Scholar
Abid, Z. et al. Synergism of Co/Na in BiVO4 microstructures for visible-light driven degradation of toxic dyes in water. Nanoscale Adv. 5 (2023).
Gnanamoorthy, G. et al. New orchestrated of X-CuTiAP (en, trien, ETA and DMA) nanospheres with enhanced photocatalytic and antimicrobial activities. J. Ind. Eng. Chem. 110, 503–519 (2022).
Article CAS Google Scholar
Patil, M. R., Khairnar, S. D. & Shrivastava, V. Synthesis, characterisation of polyaniline–Fe3O4 magnetic nanocomposite and its application for removal of an acid violet 19 dye. Appl. Nanosci. 6(4), 495–502 (2016).
Article CAS ADS Google Scholar
Sugimoto, M. The past, present, and future of ferrites. J. Am. Ceram. Soc. 82(2), 269–280 (1999).
Article CAS Google Scholar
Ding, R.-R. et al. Oxygen vacancy on hollow sphere CuFe2O4 as an efficient Fenton-like catalysis for organic pollutant degradation over a wide pH range. Appl. Catal. B 291, 120069 (2021).
Article CAS Google Scholar
Prashanth, P. et al. Synthesis, characterizations, antibacterial and photoluminescence studies of solution combustion-derived α-Al2O3 nanoparticles. J. Asian Ceram. Soc. 3(3), 345–351 (2015).
Article Google Scholar
Arifin, M. N. et al. Synthesis of titania doped copper ferrite photocatalyst and its photoactivity towards methylene blue degradation under visible light irradiation. Bull. Chem. React. Eng. Catal. 14(1), 219 (2019).
Article CAS Google Scholar
Amulya, M. S. et al. Evaluation of bifunctional applications of CuFe2O4 nanoparticles synthesized by a sonochemical method. J. Phys. Chem. Solids 148, 109756 (2021).
Article CAS Google Scholar
Kharisov, B. I., Dias, H. R. & Kharissova, O. V. Mini-review: Ferrite nanoparticles in the catalysis. Arab. J. Chem. 12(7), 1234–1246 (2019).
Article CAS Google Scholar
Khairnar, S. D., Patil, M. R. & Shrivastava, V. S. Hydrothermally synthesized nanocrystalline Nb2O5 and its visible-light photocatalytic activity for the degradation of congo red and methylene blue. Iran. J. Catal. 8(2), 143–150 (2018).
CAS Google Scholar
Koli, P. B. et al. Transition metal incorporated, modified bismuth oxide (Bi2O3) nano photo catalyst for deterioration of rosaniline hydrochloride dye as resource for environmental rehabilitation. J. Indian Chem. Soc. 98(11), 100225 (2021).
Article CAS Google Scholar
Li, R. et al. Construction of heterostructured CuFe2O4/g-C3N4 nanocomposite as an efficient visible light photocatalyst with peroxydisulfate for the organic oxidation. Appl. Catal. B 244, 974–982 (2019).
Article CAS Google Scholar
Zhao, W. et al. A simple method for fabricating p–n junction photocatalyst CuFe2O4/Bi4Ti3O12 and its photocatalytic activity. Mater. Chem. Phys. 143(3), 952–962 (2014).
Article CAS Google Scholar
Keerthana, S. et al. Pure and Ce-doped spinel CuFe2O4 photocatalysts for efficient rhodamine B degradation. Environ. Res. 200, 111528 (2021).
Article CAS PubMed Google Scholar
Dayana, P. N. et al. Zirconium doped copper ferrite (CuFe2O4) nanoparticles for the enhancement of visible light-responsive photocatalytic degradation of rose Bengal and indigo carmine dyes. J. Cluster Sci. 33(4), 1739–1749 (2022).
Article CAS Google Scholar
Pallavolu, M. R. et al. Bio-derived graphitic carbon quantum dot encapsulated S-and N-doped graphene sheets with unusual battery-type behavior for high-performance supercapacitor. Carbon 202, 93–102 (2023).
Article CAS Google Scholar
Qin, X. et al. Nitrogen-and sulfur-doped graphene quantum dots for chemiluminescence. Nanoscale 5(8), 3864–3871 (2023).
Article Google Scholar
Rati, Y. et al. Visible light assisted degradation of Rhodamin B by reusable S-doped ZnO thin film photocatalyst. Opt. Mater. 135, 113370 (2023).
Article CAS Google Scholar
Patil, A. B., Patil, K. R. & Pardeshi, S. K. Ecofriendly synthesis and solar photocatalytic activity of S-doped ZnO. J. Hazard. Mater. 183(1), 315–323 (2010).
Article CAS PubMed Google Scholar
Sreekala, G. et al. Removal of lead (II) ions from water using copper ferrite nanoparticles synthesized by green method. Mater. Today Proc. 45, 3986–3990 (2021).
Article CAS Google Scholar
Rezaul Karim, K. M. et al. Photoelectrocatalytic reduction of carbon dioxide to methanol using CuFe2O4 modified with graphene oxide under visible light irradiation. Ind. Eng. Chem. Res. 58(2), 563–572 (2019).
Article CAS Google Scholar
Khairnar, S. D. et al. Synthesis and characterization of 2-D La-doped Bi2O3 for photocatalytic degradation of organic dye and pesticide. J. Photochem. Photobiol. 6, 100030 (2021).
Article Google Scholar
Kumar, A. et al. Greener route for synthesis of aryl and alkyl-14H-dibenzo [aj] xanthenes using graphene oxide-copper ferrite nanocomposite as a recyclable heterogeneous catalyst. Sci. Rep. 7(1), 1–18 (2017).
Mirzaeifard, Z. et al. ZnO photocatalyst revisited: Effective photocatalytic degradation of emerging contaminants using S-doped ZnO nanoparticles under visible light radiation. Ind. Eng. Chem. Res. 59(36), 15894–15911 (2020).
Article CAS Google Scholar
Luo, L. et al. High lithium electroactivity of electrospun CuFe2O4 nanofibers as anode material for lithium-ion batteries. Electrochim. Acta 144, 85–91 (2014).
Article CAS Google Scholar
Maleki, A., Hajizadeh, Z. & Salehi, P. Mesoporous halloysite nanotubes modified by CuFe2O4 spinel ferrite nanoparticles and study of its application as a novel and efficient heterogeneous catalyst in the synthesis of pyrazolopyridine derivatives. Sci. Rep. 9(1), 1–8 (2019).
Article Google Scholar
Hoa, P. et al. Gas sensing properties of CuFe2O4 nanoparticles prepared by spray co-precipitation method. Vietnam J. Chem. 57, 32–38 (2019).
Article CAS Google Scholar
Oliveira, T. P. et al. Synthesis, characterization, and photocatalytic investigation of CuFe2O4 for the degradation of dyes under visible light. Catalysts 12(6), 623 (2022).
Article CAS Google Scholar
Hussain, E. et al. Titania-supported palladium/strontium nanoparticles (Pd/Sr-NPs@P25) for photocatalytic H2 production from water splitting. J. Phys. Chem. C 120(31), 17205–17213 (2016).
Article CAS Google Scholar
Attia, S. et al. Effect of Ni toward the optical and transport properties of the spinel solid solution NixCu1−xFe2O4 nanoparticles. J. Environ. Chem. Eng. 10(6), 108601 (2022).
Article CAS Google Scholar
Selima, S. S., Khairy, M. & Mousa, M. A. Comparative studies on the impact of synthesis methods on structural, optical, magnetic and catalytic properties of CuFe2O4. Ceram. Int. 45(5), 6535–6540 (2019).
Article CAS Google Scholar
Amuthan, T. et al. A novel p-CuFe2O4/n-ZnS heterojunction photocatalyst: Co-precipitation synthesis, characterization and improved visible-light driven photocatalytic activity for removal of MB and CV dyes. Phys. B 638, 413842 (2022).
Article CAS Google Scholar
Link, S. & El-Sayed, M. A. Shape and size dependence of radiative, non-radiative and photothermal properties of gold nanocrystals. Int. Rev. Phys. Chem. 19(3), 409–453 (2000).
Article CAS Google Scholar
Hammad, T. M. et al. Optical and magnetic characterizations of zinc substituted copper ferrite synthesized by a co-precipitation chemical method. J. Alloy. Compd. 741, 123–130 (2018).
Article CAS Google Scholar
Graetzel, M. et al. Materials interface engineering for solution-processed photovoltaics. Nature 488(7411), 304–312 (2012).
Article CAS PubMed ADS Google Scholar
Hussain, E. et al. Remarkable effect of BaO on photocatalytic H2 evolution from water splitting via TiO2 (P25) supported palladium nanoparticles. J. Environ. Chem. Eng. 7(1), 102729 (2019).
Article CAS Google Scholar
Qian, R. et al. Charge carrier trapping, recombination and transfer during TiO2 photocatalysis: An overview. Catal. Today 335, 78–90 (2019).
Article CAS Google Scholar
Chang, S. et al. High-efficiency and selective adsorption of organic pollutants by magnetic CoFe2O4/graphene oxide adsorbents: Experimental and molecular dynamics simulation study. Sep. Purif. Technol. 238, 116400 (2020).
Article CAS Google Scholar
Liu, T. et al. Molecular structure perspective on Temperature-Sensitive properties of rhodamine aqueous solutions. Spectrochim. Acta Part A Mol. Biomol. Spectrosc. 275, 121166 (2022).
Article CAS Google Scholar
Shao, Y. et al. The photoluminescence of rhodamine B encapsulated in mesoporous Si-MCM-48, Ce-MCM-48, Fe-MCM-48 and Cr-MCM-48 molecular sieves. J. Photochem. Photobiol. A 180(1), 59–64 (2006).
Article CAS ADS Google Scholar
Zhong, H. et al. Microwave photocatalytic degradation of Rhodamine B using TiO2 supported on activated carbon: Mechanism implication. J. Environ. Sci. 21(2), 268–272 (2009).
Article Google Scholar
Zhuang, J. et al. Photocatalytic degradation of RhB over TiO2 bilayer films: Effect of defects and their location. Langmuir 26(12), 9686–9694 (2010).
Article CAS PubMed Google Scholar
Malwal, D. & Gopinath, P. Enhanced photocatalytic activity of hierarchical three dimensional metal oxide@CuO nanostructures towards the degradation of Congo red dye under solar radiation. Catal. Sci. Technol. 6(12), 4458–4472 (2016).
Article CAS Google Scholar
Movahedi, M., Mahjoub, A. R. & Janitabar-Darzi, S. Photodegradation of Congo red in aqueous solution on ZnO as an alternative catalyst to TiO2. J. Iran. Chem. Soc. 6(3), 570–577 (2009).
Article CAS Google Scholar
Lü, X.-F. et al. Degradation of methyl orange by UV, O3 and UV/O3 systems: Analysis of the degradation effects and mineralization mechanism. Res. Chem. Intermed. 39(9), 4189–4203 (2013).
Article Google Scholar
Basahel, S. N. et al. Influence of crystal structure of nanosized ZrO2 on photocatalytic degradation of methyl orange. Nanoscale Res. Lett. 10(1), 73 (2015).
Article PubMed PubMed Central ADS Google Scholar
Sha, Y. et al. Rapid degradation of azo dye methyl orange using hollow cobalt nanoparticles. Chemosphere 144, 1530–1535 (2016).
Article CAS PubMed ADS Google Scholar
Zhang, Y. et al. Oxidation characteristics and degradation potential of a dye-decolorizing peroxidase from Bacillus amyloliquefaciens for crystal violet dye. Biochem. Eng. J. 168, 107930 (2021).
Article CAS Google Scholar
Soliman, A. M. et al. Photocatalytic activity of transition metal ions-loaded activated carbon: Degradation of crystal violet dye under solar radiation. J. Water Process Eng. 17, 245–255 (2017).
Article Google Scholar
Vosoughifar, M. Preparation and application of copper ferrite nanoparticles for degradation of methyl orange. J. Mater. Sci. Mater. Electron. 27(10), 10449–10453 (2016).
Article CAS Google Scholar
Rahimi-Nasrabadi, M. et al. Nanocrystalline Ce-doped copper ferrite: Synthesis, characterization, and its photocatalyst application. J. Mater. Sci. Mater. Electron. 27(11), 11691–11697 (2016).
Article CAS Google Scholar
Ahmadi, H. et al. Nanocrystalline CuFe2−xSmxO4: Synthesis, characterization and its photocatalytic degradation of methyl orange. J. Mater. Sci. Mater. Electron. 27(5), 4689–4693 (2016).
Article CAS Google Scholar
Nasiri, A. et al. Nanocrystalline copper ferrite: Synthesis of different shapes through a new method and its photocatalyst application. J. Mater. Sci. Mater. Electron. 28(3), 2401–2406 (2017).
Article CAS Google Scholar
Ruby, S. et al. Sunlight-driven photocatalytic degradation of methyl orange based on bismuth ferrite (BiFeO3) heterostructures composed of interconnected nanosheets. J. Nanosci. Nanotechnol. 20(3), 1851–1858 (2020).
Article CAS PubMed Google Scholar
Lu, C. et al. Facile fabrication of heterostructured cubic-CuFe2O4/ZnO nanofibers (c-CFZs) with enhanced visible-light photocatalytic activity and magnetic separation. RSC Adv. 6(111), 110155–110163 (2016).
Article CAS ADS Google Scholar
Das, K. C. et al. Sn (II) inserted on hydroxyapatite encapsulated nickel ferrite (NiFe2O4@HAp-Sn2+): A novel nanocomposite for the effective photo-degradation of rhodamine B dye. J. Clean. Prod. 290, 125172 (2021).
Article CAS Google Scholar
Hariani, P. L. et al. Preparation of NiFe2O4 nanoparticles by solution combustion method as photocatalyst of Congo red. Bull. Chem. React. Eng. Catal. 16(3), 481–490 (2021).
Article CAS Google Scholar
Jadhav, S. D. & Patil, R. Photocatalytic degradation study of Methyl Orange and Congo red using Mg-Co ferrite powder. J. Water Environ. Nanotechnol. 7(2), 170–179 (2022).
CAS Google Scholar
Maruthupandy, M. et al. Development of chitosan decorated Fe3O4 nanospheres for potential enhancement of photocatalytic degradation of Congo red dye molecules. Spectrochim. Acta Part A Mol. Biomol. Spectrosc. 267, 120511 (2022).
Article CAS Google Scholar
Jasrotia, R. et al. Robust and sustainable Mg1-xCexNiyFe2-yO4 magnetic nanophotocatalysts with improved photocatalytic performance towards photodegradation of crystal violet and rhodamine B pollutants. Chemosphere 294, 133706 (2022).
Article CAS PubMed ADS Google Scholar
Liu, X. et al. Microwave-assisted catalytic degradation of crystal violet with barium ferrite nanomaterial. Ind. Eng. Chem. Res. 55(46), 11869–11877 (2016).
Article CAS Google Scholar
Zhang, X. et al. Potassium ferrite as heterogeneous photo-fenton catalyst for highly efficient dye degradation. Catalysts 10(3), 293 (2020).
Article Google Scholar
Masunga, N. et al. Recent advances in copper ferrite nanoparticles and nanocomposites synthesis, magnetic properties and application in water treatment: Review. J. Environ. Chem. Eng. 7(3), 103179 (2019).
Article CAS Google Scholar
Konstantinou, I. K. & Albanis, T. A. TiO2-assisted photocatalytic degradation of azo dyes in aqueous solution: Kinetic and mechanistic investigations: A review. Appl. Catal. B 49(1), 1–14 (2004).
Article CAS Google Scholar
Rao, Z. et al. Photocatalytic oxidation mechanism of Gas-Phase VOCs: Unveiling the role of holes, ⋅ OH and ⋅ O2−. Chem. Eng. J. 430, 132766 (2022).
Article CAS Google Scholar
Ilyas, A. et al. Growth of villi-microstructured bismuth vanadate (Vm-BiVO4) for photocatalytic degradation of crystal violet dye. RSC Adv. 13(4), 2379–2391 (2023).
Article CAS PubMed PubMed Central ADS Google Scholar
This work was finically supported by Higher Education Commission (HEC) of Pakistan (No. 377/IPFP-II)(Batch-I/)SRGP/NAHE/HEC/2020/27 Islamabad. Synthesis work and dye degradation activities were conducted in Institute of Chemistry, The Islamia University of Bahawalpur (Inorganic Material Laboratory (52s). Dr. Ejaz Hussain acknowledges Syed Babar Ali School of Science and engineering, Lahore University of Management Sciences (LUMS) to facilitate for characterization of samples.
Institute of Chemistry, Inorganic Materials Laboratory 52S, The Islamia University of Bahawalpur, Bahawalpur, 63100, Pakistan
Anam Aslam, Muhammad Zeeshan Abid, Khezina Rafiq, Abdul Rauf & Ejaz Hussain
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
A.A and M.Z.A completed the synthesis work. K.R prepared and edited manuscript, A.R facilitated characterization of samples. E.H supervised the work, finalized and submitted the manuscript.
The authors declare no competing interests.
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
Aslam, A., Abid, M.Z., Rafiq, K. et al. Tunable sulphur doping on CuFe2O4 nanostructures for the selective elimination of organic dyes from water. Sci Rep 13, 6306 (2023). https://doi.org/10.1038/s41598-023-33185-0
DOI: https://doi.org/10.1038/s41598-023-33185-0
Anyone you share the following link with will be able to read this content:
Sorry, a shareable link is not currently available for this article.
Provided by the Springer Nature SharedIt content-sharing initiative
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.
Scientific Reports (Sci Rep) ISSN 2045-2322 (online)